Type: | Journal article |
Title: | Fracture resistance and microtensile bond strength of maxillary premolars restored with two resin composite inlay systems |
Author: | Sun, Y. Chen, Y. Smales, R. Yip, K. |
Citation: | American Journal of Dentistry, 2008; 21(2):97-100 |
Publisher: | Mosher & Linder Inc |
Issue Date: | 2008 |
ISSN: | 0894-8275 |
Statement of Responsibility: | Sun Ya-Shou, Chen Ya-Ming, Smales Roger J and Yip Kevin H K |
Abstract: | PURPOSE: To compare the in vitro fracture resistance and the microtensile bond strength (muTBS) of premolar teeth restored with two light-cured resin composite inlay systems. METHODS: 50 sound human maxillary premolars were divided randomly into five equal groups. Four groups received mesial-occlusal-distal (MOD) inlay preparations. Restorative treatments comprised: Group 1 (Renew direct resin composite), Group 2 (Renew direct resin composite inlay), Group 3 (Tescera indirect resin composite inlay), Group 4 (non-restored), Group 5 (intact). All teeth were loaded axially until fracture. The same resin-based materials as used in Groups 1-3 were bonded to the superficial coronal dentin of 15 teeth. Beams approximately 1.0 mm x 1.0 mm were prepared and tested in microtensile mode. Results were compared using one-way ANOVA and Tukey's multiple comparison tests. RESULTS: Mean fracture strengths (KN): Group 1, 2.06 (0.76); Group 2, 2.30 (0.49); Group 3, 2.62 (0.68); Group 4, 1.24 (0.44); Group 5, 2.40 (0.71). Group 4 was significantly weaker that the other four groups, P < 0.01. Mean muTBSs (MPa): Group 1, 33.38 (6.24); Group 2, 20.38 (6.24); Group 3, 20.87 (4.62). Group 1 was significantly stronger than the other two groups, P < 0.01. |
Keywords: | Maxilla Bicuspid Dentin Humans Tooth Fractures Aluminum Oxide Methacrylates Composite Resins Materials Testing Dental Bonding Dental Etching Acid Etching, Dental Dental Restoration Failure Inlays Dental Cavity Preparation Stress, Mechanical Tensile Strength |
Description (link): | http://www.ncbi.nlm.nih.gov/pubmed/18578176 |
Appears in Collections: | Aurora harvest Dentistry publications |
Files in This Item:
There are no files associated with this item.
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.